White, highly translucent zirconium oxide.
Advantages and indication:

for multiple indications – from veneers to wide span bridges supported by implants
highly translucent and extremely stable: flexural strength 1400 MPa, hardness 1300 HV
natural translucency for aesthetic monolithic restorations
flexible sintering temperature 1450 °C - 1550 °C / 2642 °F - 2822 °F
extremely high-precision fitting thanks to Instant Fit Process (I.F.P.)

Also available in semi-translucent (Nacera^® Shell white).

Impact resistance 8 MPa m^1/2

Solubility < 10 µg/cm²

Density > 6.04 g/cm³

ø 98.3 mm

WAK 10 ⋅ 10^-6 K^-1

Medium grain size < 0.4 µm

Material ZrO₂ 3Y-TZP

Color White, highly translucent

4 point flexural strength (Mpa) 1200 MPa

Radioactivity < 0.02 Bq/g

Thickness 12 mm

Thermal conductivity 2 W/mK

Hardness 1300 HV 0.5

Compression resistance 3000 MPa

The values listed were measured on test samples and are typical for the material. The product properties may, however, deviate from these values depending on the component design and the forming process.